The photocatalytic performance of a composite based on the association of TiO2 and 2.5 wt.% of zinc(II) phthalocyanine (TiO2/ZnPc) was evaluated towards the mineralization of paracetamol and compared to that observed for the bare oxide in different pH and H2O2 concentrations. The results show that the photocatalytic performances were influenced by the pH, with maximum efficiency around the isoelectric point. Mineralization efficiencies between 86-91% was obtained using TiO2/ZnPc in pH 5.5-6.8, with 33 mg L-1 of H2O2, ca. 15% higher than that observed with TiO2. The mineralization efficiencies using bare TiO2 and TiO2/ZnPc were respectively 112 and 18% lower in the absence of H2O2. The better performance of TiO2/ZnPc is related to its extended light absorption and non-uniform coating of the TiO2 surface by ZnPc aggregates. Above pH 6.8, the mineralization efficiencies decrease for both photocatalysts, although the consumption of H2O2 remains above 90%, due to its decomposition in alkaline pH.

In this study, we evaluated the combination between an electrochemical process, occurring in the dark, and a heterogeneous photocatalytic process for dye degradation, using the azo dye tartrazine as model of oxidizable substrate. TiO2 P25 and an Ag-doped TiO2 were used as photocatalysts in suspensions containing 50 mg L–1 of tartrazine. The best result, 74% of dye mineralization in 120 min of reaction, was obtained using TiO2 P25 as photocatalyst and a current density of 10 mA cm–2 in the electrochemical cell, a value 30% higher than the sum of the results obtained by heterogeneous photocatalysis (44%) and electrochemical oxidation (13%). The use of Ag-doped TiO2 did not result in significant improvement on tartrazine mineralization, due to the aggregation of these nanoparticles. Our results suggest that this process can be an alternative for a complete treatment (discoloration and mineralization) of tartrazine and most likely other azo dyes.

Crystalline (BiO)2CO3 nanosheets were synthesized by a rapid one-step reaction via microwave-assisted hydrothermal method using urea as a morphology mediator and carbon source. The hydrothermal method combined with microwave heating allowed to obtain sheet-like (BiO)2CO3 particles at shorter reaction times when compared to the conventional heating hydrothermal method. The photocatalytic activity of the as prepared samples was evaluated towards degradation of Ponceau 4R (C.I. 16255) under artificial UV-Vis light irradiation. The results show that good photocatalytic efficiency can be obtained for powders prepared with reaction times as low as 2 minutes.